Tensile properties of Zr70Ni16Cu6Al8 BMG at room and cryogenic temperatures
Journal article, Peer reviewed
MetadataVis full innførsel
The mechanical behaviour in tension of a hypoeutectic Zr70Ni16Cu6Al8 Bulk Metallic Glass (BMG) was studied at room (295 K) and cryogenic temperatures (150 K and 77 K) using various strain rates between 10−4 and 10−1 s−1. The yield strength was found to increase at lower temperatures with average values increasing by 16%, from 1503 MPa at 295 K to 1746 MPa at 77 K. The Zr-based BMG was found to exhibit tensile plastic elongation of about 0.4% before fracture at room temperature and high strain rates (10−1 s−1). Even higher tensile plasticity was recorded at low temperatures; plastic deformation was found highest at the intermediate temperature (150 K) reaching remarkable plastic strains in the order of 3.9%, while values up to 1.5% were recorded at 77 K. The lateral surface of the tensile specimens was observed in-situ during deformation using a high frame rate camera offering interesting insights with regard to the deformation mechanisms. Room temperature plasticity occurred through the formation and interaction of several nucleated shear bands before critical failure, while at intermediate and liquid nitrogen temperatures, most of the plastic deformation was accommodated through stable flow within a single shear band.